Specification Sheet

Application(s):
water, acid, grease and oil resistance.
Note:
and replace as necessary.
Adhesive:
Carrier:
Total Thickness:
Grit Size: 46-Grit Silicon Carbid Mineral Abrasive
Liner:
Tape Application:
Cleaning:
Shelf Life:
Kinetic Friction 1.386 Leather
ASTM D1894-06 1.136 Rubber
Property: Test Method: Measurement:
PVC Film
Thickness PSTC-33 0.15mm (6 mils)
Tensile Strength MD ASTM-D638 4.2 Kg/15mm (15.4 lbs/inch)
Tensile Strength CD ASTM-D638 3.1 Kg/15mm (11.4 lbs/inch)
Elongation ASTM-D638 200% +/- 25%
Acrylic Adhesive
Dry Coat Weight PSTC-33
44.4 g/m
2
Coating Thickness PSTC-33 0.06mm (0.0023")
Residual Solvent > 0.5%
Tack PSTC-6 20 cm (8 inch)
Shear Resistance PSTC-7 24 hours (1" x 1" @ 1 Kg)
180 Peel Adhesion PSTC-1 2.5 Kg/25mm (5 lb/inch)
Operational Temp.
(-29
0
C to 65
0
C) -20
0
F to 150
0
F
Min Application Temp.
10
0
C (50
0
F)
TRUE GRIP® (46-GRIT)
PRODUCT INFORMATION GUIDE
Anti-slip grit tape products are a fast, easy way to reduce slip and fall accidents in
Brown Kraft Paper Liner 0.005" (0.127mm)
the workplace. Tape will adhere to any clean dry surface including metal, wood and
Vinyl (6 mil) with Silicon Carbide Grit Material (46-Grit)
Slip resistant tapes are subject to wear that may reduce their performance. Inspect
concrete. Surface is constructed of a silicon carbide grit compound securely
bonded to a vinyl substrate with an aggressive acrylic adhesive. Tape is available
Acrylic Solvent Adhesive
0.035" ( 0.889mm )
in black only. Intended for both indoor and outdoor applications, and offers good
This data is based on typical results achieved. It is the sole responsibility of the buyer or user to ensure that the product is suitable
Minimum application temperature 10
0
C (50
0
F)
Surface must be clean and free from dust, dirt, oil, wax, silicone.
Clean tape surface with a mild soap and light broom, rinse with fresh water.
One year from date of purchase when stored at 70
0
F, 50% relative humidity.
for any proposed end use or application and to ensure proper cleaning of the substrate to which it will be applied. This data in no
way constitutes a specification, nor should it be seen as a recommendation for use. We accept no liability for any loss, damage
or injury resulting from the use of these products or data. March 2013.