Information

Note:
- When printing with PolyLite™ PC it is recommended to use an enclosure. For
large part it is recommended to use a heated chamber.
- It is recommended to anneal the printed part right after the printing process to
release the residual internal stress. Annealing settings: 100˚C for 2h
Property
Testing Method
Typical Value
Young’s modulus (X-Y)
ISO 527, GB/T 1040
2307 ± 60 MPa
Young’s modulus (Z)
2260 ± 137 MPa
Tensile strength (X-Y)
ISO 527, GB/T 1040
62.7 ± 1.3 MPa
Tensile strength (Z)
41.9 ± 2.1 MPa
Elongation at break (X-Y)
ISO 527, GB/T 1040
3.15 ± 0.35 %
Elongation at break (Z)
2.2 ± 0.2 %
Bending modulus (X-Y)
ISO 178, GB/T 9341
2247 ± 159 MPa
Bending modulus (Z)
N/A
Bending strength (X-Y)
ISO 178, GB/T 9341
100.4 ± 2.1 MPa
Bending strength (Z)
N/A
Charpy impact strength (X-Y)
ISO 179, GB/T 9343
3.41 ± 0.03 kj/m
2
Charpy impact strength (Z)
N/A
Low temperature impact
strength (X-Y)
ISO 179-1/1eA:2010,
-30° C
9.8 ± 0.5 kj/m
2
Printing temperature
255 °C
Bed temperature
100 °C
Shell
2
Top & bottom layer
4
Infill
100%
Environmental temperature
70 – 80 (recommended) (˚C)
Cooling fan
OFF