PolyMax™ PLA is an incredibly easy-to-print filament with improved me-
chanical properties, making it an excellent alternative to ABS.
Available colors:
Diameter accuracy (2.85/1.75 mm): Weight accuracy:
Physical properties
Mechanical properties
Drying settings
Property
Property
Melt Index 210 °C, 2.6 kg
Tensile strength (X-Y) ASTM D638 (ISO 527, GB/T 1040) 28.1 ± 1.3 (MPa)
Bending modulus ASTM D790 (ISO 178, GB/T 9341) 2119 ± 60 (MPa)
Testing method
Testing method
Typical value
Typical value
Glass transition temperature DSC, 10 °C/min
Elongation at break (X-Y) ASTM D638 (ISO 527, GB/T 1040) 1.4 ± 0.3 (%)
Density ASTM D792 (ISO 1183, GB/T 1033) 1.17 – 1.24 (g/cm
3
at 21.5 °C)
61 (°C)
62 (°C)
5-8 (g/10 min)
Young’s modulus (X-Y) ASTM D638 (ISO 527, GB/T 1040) 1879 ± 109 (MPa)
Bending strength ASTM D790 (ISO 178, GB/T 9341) 48.0 ± 1.9 (MPa)
Charpy impact strength ASTM D256 (ISO 179, GB/T 1043) 12.2 ± 1.03 (kJ/m
2
)
Vicat softening temperature ASTM D1525 (ISO 306, GB/T 1633)
600g +/- 20g
750g +/- 20g
1000g +/- 30g
3000g +/- 60g
70% is within +/- 0.01
97% is within +/- 0.02
99% is within +/- 0.03
99.9% is within +/- 0.04
80˚C for 8h
Melting temperature
Crystallization temperature
DSC, 10 °C/min
DSC, 10 °C/min
149 (°C)
149 (°C)