Datasheet

Note:
- When printing with PolyMax™ PC it is recommended to use an enclosure. For
large part it is recommended to use a heated chamber.
- It is recommended to anneal the printed part right after the printing process to
release the residual internal stress. Annealing settings: 100˚C for 2h
-
Property
Testing Method
Typical Value
Young’s modulus (X-Y)
ISO 527, GB/T 1040
2048 ± 66 MPa
Young’s modulus (Z)
1845 ± 35 MPa
Tensile strength (X-Y)
ISO 527, GB/T 1040
59.7 ± 1.8 MPa
Tensile strength (Z)
29.1 ± 4.1 MPa
Elongation at break (X-Y)
ISO 527, GB/T 1040
12.24 ± 1.44 %
Elongation at break (Z)
1.84 ± 0.14 %
Bending modulus (X-Y)
ISO 178, GB/T 9341
2044 ± 58 MPa
Bending modulus (Z)
N/A
Bending strength (X-Y)
ISO 178, GB/T 9341
94.1 ± 0.9 MPa
Bending strength (Z)
N/A
Charpy impact strength (X-Y)
ISO 179, GB/T 9343
25.1 ± 1.9 kj/m
2
Charpy impact strength (Z)
N/A
Printing temperature
255 °C
Bed temperature
100 °C
Shell
2
Top & bottom layer
4
Infill
100%
Environmental temperature
70 – 80 (recommended) (˚C)
Cooling fan
OFF