Information

6
PolyLite
TM
PC
PolyLite™ PC is produced using a polycarbonate resin specifically engi-
neered for 3D printing. It delivers good stiness and heat resistance with
light diusing properties.
Available colors:
Diameter accuracy (2.85/1.75 mm): Weight accuracy:
Physical properties
Mechanical properties
Drying settings
Property
Property
Melt Index 260 °C, 1.2 kg
Tensile strength (X-Y) ASTM D638 (ISO 527, GB/T 1040) 62.7 ± 1.3 (MPa)
Bending modulus ASTM D790 (ISO 178, GB/T 9341) 2477 ± 159 (MPa)
Testing method
Testing method
Typical value
Typical value
Glass transition temperature DSC, 10 °C/min
Elongation at break (X-Y) ASTM D638 (ISO 527, GB/T 1040) 3.2 ± 0.4 (%)
Density ASTM D792 (ISO 1183, GB/T 1033) 1.19 – 1.20 (g/cm
3
at 21.5 °C)
113 (°C)
119 (°C)
8-11 (g/10 min)
Young’s modulus (X-Y) ASTM D638 (ISO 527, GB/T 1040) 2307 ± 60 (MPa)
Bending strength ASTM D790 (ISO 178, GB/T 9341) 100.4 ± 2.7 (MPa)
Charpy impact strength ASTM D256 (ISO 527, GB/T 1040) 3.4 ± 0.1 (kJ/m
2
)
Vicat softening temperature ASTM D1525 (ISO 306, GB/T 1633)
600g +/- 20g
750g +/- 20g
1000g +/- 30g
3000g +/- 60g
70% is within +/- 0.01
97% is within +/- 0.02
99% is within +/- 0.03
99.9% is within +/- 0.04
80˚C for 8h
Decomposition temperature TGA, 20 °C/min 129- 132 (°C)