Data Sheet

MATERIAL DATASHEET
Mechanical Properties Metric Imperial Standard
Tensile Modulus
6 500 MPa
943 ksi
ISO 527
1 mm/min
(0.04 inch/min)
Tensile Strength (Yield)
60 MPa
8,700 psi
ISO 527
1 mm/min
(0.04 inch/min)
Tensile Strength (Break)
60 MPa
8
,700 psi
ISO 527
1 mm/min
(0.04 inch/min)
Elongation (Break)
1.6 %
1.6 %
ISO 527
1 mm/min
(0.04
inch/min)
Flexural Modulus
4 300 MPa
624 ksi
ISO 178
2 mm/min
(0.08 inch/min)
Flexural Strength (Yield)
83 MPa
12,000 psi
ISO 178
2 mm/min
(0.08 inch/min)
Flexural Strength (Break)
78 MPa
11,300 psi
ISO 178
2 mm/min
(0.08 inch/min)
Physical Properties Metric Imperial Standard
Density
0,94 g/cm
3
7,85 lbs
/gal
ISO 1183-
A
Moisture Absorption
Very low (<0.1%)
Very low (<0.1%)
ISO 62
23 °
C / 50% RH
Water Absorption
Very low (<0.1%)
Very low (<0.1%)
ISO 62
23 °
C / Sat
Thermal Properties Metric Imperial Standard
Filament diameter
1,75 mm / 2,85 mm
0,069 inch / 0,112 inch
+/-
0,05 mm
Material weight
500 g / 2200
g
1.1 lbs / 4.85 lbs
Net weight
Spool (500g / 1.1lbs)
200 / 52 / 55 mm
7.9 / 2.0 / 2.2 inch
Øext / Øint / width
Spool (2200g / 4.85 lbs)
300
/ 52 / 102 mm
11.8 / 2.0 / 4.0 inch
Øext / Øint / width
PACKAGING
Thermal Properties Metric Imperial Standard
Heat Deflection
Temperature
120 °
C
248 °
F
ISO 75
Method A (1.8 MPa)
Melting Point
167 °
C
333 °
F
ISO 11357
Printer Settings Nozzle Bed
Recommended
Bed Type
Temperature
220 °C - 280 °
C
80 °C - 110 °
C
1) Perforated plate
2) HDPE sheet
3) PP adhesive
Printing
speed 30-
100 mm/s
-
Nozzle
diameter
> 0.4 mm
-
Copyright © 2017 Owens Corning. All Rights Reserved.
DESCRIPTION
Developed by Owens Corning, a world leader in composite solutions,
XSTRAND™ GF30-PP filament for 3D printing is a reinforced material
designed to be compatible with any standard Fused Filament Fabrication
3D printer (1.75 and 2.85 mm diameters available).
BENEFITS & PERFORMANCES
▪ High stiffness and strength (up to +200% compare to ABS)
▪ Large operational temperature range (-20°C to 120°C)
▪ Very good chemical and UV resistance
▪ Very low moisture absorption
▪ Excellent layer adhesion
▪ Reduced warping effect compared to neat PP
POTENTIAL APPLICATIONS
XSTRAND™ GF30-PP is designed for functional prototyping and
demanding applications such as industrial tooling, transportation,
electronics, small appliances, sports & leisure...