ManualsBrandsOrfit ManualsMedical & LaboratoryOrfilight® Black NS Splinting Material, 18" x 24" x 3/32", Micro Perforated

TECHNICAL DATA SHEET

ORFILIGHT®

1.6 mm (1/16”)

Thickness

mm (inches)

1.6 (1/16)

Perforation

% (type)

13 (micro)

Thermoforming conditions

Optimum activation temperature (in water bath)

°C (°F)

65 (149)

Activation time (in water bath)

minutes

3 - 4

Transparent when activated

Working time

minutes

1 - 1 ½

Hardening time

minutes

1 ¾ - 2 ¼

Time to completion

minutes

10 - 11

Resistance to stretch

moderate

Drape

high

Memory (after 200 % elongation)

high

Maximum elongation when activated

1800

Memory (after maximum elongation)

high

Sticks to itself when activated and wet

yes

Sticks to itself when activated, after drying

reliable under

high stress

Adhesion (velcro strip) using heat gun

yes

Mechanical properties at 21°C

Flexural modulus

MPa

260

Elastic modulus

MPa

170

Tensile strength

MPa

8.0

Strain at break

General properties

Density

g cm

0.85

Hardness (shore D)

Surface feeling

smooth

Color

skin

Odor

none

Fatigue

cycles

> 10000

Biocompatible

yes

Summary of content (10 pages)

PAGE 1
TECHNICAL DATA SHEET ORFILIGHT® 1.6 mm (1/16”) Thickness Perforation mm (inches) % (type) 1.
PAGE 2
TECHNICAL DATA SHEET ORFILIGHT® 2.5 mm (3/32”) Thickness Perforation mm (inches) % (type) 2.
PAGE 3
TECHNICAL DATA SHEET ORFILIGHT® 3.2 mm (1/8”) Thickness Perforation mm (inches) % (type) 3.2 (1/8) 0 (non perfo) 3.2 (1/8) 3.
PAGE 4
TECHNICAL DATA SHEET ORFILIGHT® BLACK NS 1.6 mm (1/16”) Thickness Perforation mm (inches) % (type) 1.
PAGE 5
TECHNICAL DATA SHEET ORFILIGHT® BLACK NS 2.5 mm (3/32”) Thickness Perforation mm (inches) % (type) 2.
PAGE 6
TECHNICAL DATA SHEET ORFILIGHT® BLACK NS 3.2 mm (1/8”) Thickness Perforation mm (inches) % (type) 3.2 (1/8) 0 (non perfo) 3.2 (1/8) 3.5 (mini) °C (°F) minutes 65 (149) 3-4 no 2-2½ 4¾-5¼ 20 - 21 65 (149) 3-4 no 1¾-2¼ 3¾-4¼ 15 - 16 moderate high high 2300 high moderate high high 2200 high yes reliable under low stress yes reliable under low stress yes yes MPa MPa MPa % 285 145 10.0 140 285 125 8.0 20 g cm-³ 0.80 47 smooth black none > 10000 yes 0.
PAGE 7
TECHNICAL DATA SHEET ORFILIGHT® ATOMIC BLUE NS 1.6 mm (1/16”) Thickness Perforation mm (inches) % (type) 1.
PAGE 8
TECHNICAL DATA SHEET ORFILIGHT® ATOMIC BLUE NS 2.5 mm (3/32”) Thickness Perforation mm (inches) % (type) 2.
PAGE 9
TECHNICAL DATA SHEET ORFILIGHT® ATOMIC BLUE NS 3.2 mm (1/8”) Thickness Perforation mm (inches) % (type) 3.2 (1/8) 0 (non perfo) 3.2 (1/8) 3.5 (mini) °C (°F) minutes 65 (149) 3-4 no 2-2½ 4¾-5¼ 20 - 21 65 (149) 3-4 no 1¾-2¼ 3¾-4¼ 15 - 16 moderate high high 2300 high moderate high high 2200 high yes reliable under low stress yes reliable under low stress yes yes MPa MPa MPa % 285 145 10.0 140 285 125 8.0 20 g cm-³ 0.80 47 smooth atomic blue none > 10000 yes 0.
PAGE 10
TECHNICAL DATA SHEET INFORMATION The hardening time indicates the time period during which the material remains flexible, but no longer mouldable. The time to completion indicates the length of time until the orthosis is finished and can be worn by the patient. The memory indicates the ability of the material to regain its original shape after reheating. The flexural modulus indicates the resistance of the material to a force causing it to bend.