Specification Sheet

ManualsBrandsOrfit ManualsMedical & LaboratoryClassic Soft Precut Gauntlet Thumb Post Splint, 1/16" Micro Perforated, Small

TECHNICAL DATA SHEET

ORFIT

CLASSIC SOFT 1.6 mm (1/16”)

Thickness

mm (inches)

1.6 (1/16)

Perforation

% (type)

0 (non perfo)

13 (micro)

Thermoforming conditions

Optimum activation temperature (in water bath)

°C (°F)

65 (149)

Activation time (in water bath)

minutes

3 - 4

Transparent when activated

yes

Working time

minutes

1 ¼ - 1 ¾

1 - 1 ½

Hardening time

minutes

3 ¾ - 4 ¼

2 ½ - 3

Time to completion

minutes

16 - 17

13 - 14

Resistance to stretch

moderate

Drape

high

Memory (after 200 % elongation)

full

Maximum elongation when activated

1250

1050

Memory (after maximum elongation)

full

Sticks to itself when activated and wet

yes

Sticks to itself when activated, after drying

reliable under

high stress

reliable under

high stress

Adhesion (velcro strip) using heat gun

yes

Mechanical properties at 21°C

Flexural modulus

MPa

530

380

Elastic modulus

MPa

300

265

Tensile strength

MPa

20.0

15.0

Strain at break

no break

General properties

Density

g cm

1.13

Hardness (shore D)

Surface feeling

smooth

Color

skin

Odor

none

Fatigue

cycles

> 10000

Biocompatible

yes

Summary of content (8 pages)

PAGE 1
TECHNICAL DATA SHEET ORFIT® CLASSIC SOFT 1.6 mm (1/16”) Thickness Perforation mm (inches) % (type) 1.6 (1/16) 0 (non perfo) 1.6 (1/16) 13 (micro) °C (°F) minutes 65 (149) 3-4 yes 1¼-1¾ 3¾-4¼ 16 - 17 65 (149) 3-4 yes 1-1½ 2½-3 13 - 14 moderate high full 1250 full moderate high full 1050 full yes reliable under high stress yes reliable under high stress yes yes MPa MPa MPa % 530 300 20.0 no break 380 265 15.0 60 g cm-³ 1.13 60 smooth skin none > 10000 yes 1.
PAGE 2
TECHNICAL DATA SHEET ORFIT® CLASSIC SOFT 2.0 mm (1/12”) Thickness mm (inches) % (type) 2.
PAGE 3
TECHNICAL DATA SHEET ORFIT® CLASSIC SOFT 2.5 mm (3/32”) Thickness Perforation mm (inches) % (type) 2.
PAGE 4
TECHNICAL DATA SHEET ORFIT® CLASSIC SOFT 3.2 mm (1/8”) Thickness Perforation mm (inches) % (type) 3.2 (1/8) 0 (non perfo) 3.2 (1/8) 3.5 (mini) 3.
PAGE 5
TECHNICAL DATA SHEET ORFIT® CLASSIC SOFT 4.2 mm (3/16”) Thickness Perforation mm (inches) % (type) 4.2 (3/16) 0 (non perfo) 4.2 (3/16) 3.5 (mini) °C (°F) minutes 65 (149) 4-5 yes 2½-3 9-9½ 28 - 29 65 (149) 4-5 yes 2¼-2¾ 8-8½ 24 - 25 moderate high full 1425 full moderate high full 1200 full yes reliable under high stress yes reliable under high stress yes yes MPa MPa MPa % 530 300 21.5 no break 475 285 17.0 145 g cm-³ 1.13 60 smooth skin none > 10000 yes 1.
PAGE 6
TECHNICAL DATA SHEET ORFIT® CLASSIC STIFF 3.2 mm (1/8”) Thickness Perforation mm (inches) % (type) 3.2 (1/8) 0 (non perfo) 3.2 (1/8) 3.5 (mini) °C (°F) minutes 65 (149) 4-5 yes 2-2½ 7½-8 21 - 22 65 (149) 4-5 yes 1¾-2¼ 6½-7 24 - 25 high high full 1150 full high high full 1020 full yes reliable under high stress yes reliable under high stress yes yes MPa MPa MPa % 530 310 20.0 no break 485 270 16.5 45 g cm-³ 1.13 60 smooth skin none > 10000 yes 1.
PAGE 7
TECHNICAL DATA SHEET ORFIT® CLASSIC STIFF 4.2 mm (3/16”) Thickness Perforation mm (inches) % (type) 4.2 (3/16) 0 (non perfo) 4.2 (3/16) 3.
PAGE 8
TECHNICAL DATA SHEET INFORMATION The hardening time indicates the time period during which the material remains flexible, but no longer mouldable. The time to completion indicates the length of time until the orthosis is finished and can be worn by the patient. The memory indicates the ability of the material to regain its original shape after reheating. The flexural modulus indicates the resistance of the material to a force causing it to bend.