No. Item Specification Test method
11 Soldering effect
(Non-preheat)
Appearance No marked defect. The lead wire should be immersed into the melted
solder of 35010C up to about 1.5 to 2.0mm from
the main body for 3.50.5 s.
Pre-treatment : Capacitor should be stored at
852C for 1 h, then placed at
*¹room condition for 242 h before
initial measurements. (Char. B,E)
Post-treatment : Capacitor should be stored for 1 to
2 h at *¹room condition. (Char. SL)
Post-treatment : Capacitor should be stored for 4 to
24 h at *¹room condition. (Char. B,E)
Capacitance
change
Char. SL : Within  2.5%
Char. B : Within  5%
Char. E : Within  15%
Dielectric
strength
(Between
lead wires)
Per item 3.
12 Soldering effect
(On-preheat)
Appearance No marked defect. First the capacitor should be stored at 120+0/-5°C
for 60+0/-5 s.
Then, as in figure, the lead wires should be
immersed solder of 260+0/-5°C up to 1.5 to 2.0mm
from the root of terminal for 7.5+0/-1 s.
Pre-treatment : Capacitor should be stored at
852C for 1 h, then placed at
*¹room condition for 242 h before
initial measurements. (Char. B,E)
Post-treatment : Capacitor should be stored for 1 to
2 h at *¹room condition. (Char. SL)
Post-treatment : Capacitor should be stored for 4 to
24 h at *¹room condition.
(Char. B,E)
Capacitance
change
Char. SL : Within  2.5%
Char. B : Within  5%
Char. E : Within  15%
Dielectric
strength
(Between
lead wires)
Per item 3.
13 Humidity
(Under steady
state)
Appearance No marked defect.
Set the capacitor for 500 +24/-0 h at 402C in 90
to 95% relative humidity.
Pre-treatment : Capacitor should be stored at
852C for 1 h, then placed at
*¹room condition for 242 h before
initial measurements. (Char. B,E)
Post-treatment : Capacitor should be stored for 1 to
2 h at *¹room condition.
Capacitance
change
Char. SL : Within  5%
Char. B : Within 10%
Char. E : Within 20%
Q Char. SL :
275+5/2C*²min. (30pF under)
350 min. (30pF min.)
D.F. Char. B,E : 5.0% max.
I.R.
1000M min.
14 Humidity loading Appearance No marked defect.
Apply the rated voltage for 500 +24/-0 h at 402C
in 90 to 95% relative humidity.
(Charge/Discharge current50mA.)
Pre-treatment : Capacitor should be stored at
852C for 1 h, then placed at
*¹room condition for 242 h before
initial measurements. (Char. B,E)
Post-treatment : Capacitor should be stored for 1 to
2 h at *¹room condition. (Char. SL)
Post-treatment : Capacitor should be stored at
852C for 1 h, then placed at
*¹room condition for 242 h.
(Char. B,E)
Capacitance
change
Char. SL : Within  7.5%
Char. B : Within 10%
Char. E : Within 20%
Q Char. SL :
100+10/3C*²min. (30pF under)
200 min. (30pF min.)
D.F. Char. B,E : 5.0% max.
I.R.
500M min.
*¹ "room condition" Temperature: 15 to 35C, Relative humidity: 45 to 75%, Atmospheric pressure: 86 to 106kPa
*² "C" expresses nominal capacitance value (pF)