Datasheet
TDS LOCTITE
®
480™, January-2017
Cured for 30 seconds @ 22 °C
Tensile Strength, ISO 6922:
Buna-N N/mm² ≥1.8
LMS
(psi) (≥260)
Cured for 24 hours @ 22 °C
Lap Shear Strength, ISO 4587:
Steel (grit blasted) N/mm² 22 to 30
(psi) (3,200 to 4,400)
Aluminum (etched) N/mm² 14 to 22
(psi) (2,000 to 3,200)
Zinc dichromate N/mm² 8 to 15
(psi) (1,200 to 2,200)
ABS N/mm² 6 to 20
(psi) (870 to 2,900)
PVC N/mm² 4 to 20
(psi) (580 to 2,900)
Phenolic N/mm² 5 to 15
(psi) (730 to 2,200)
Polycarbonate N/mm² 5 to 20
(psi) (730 to 2,900)
Nitrile N/mm² 5 to 15
(psi) (730 to 2,200)
Neoprene N/mm² 5 to 15
(psi) (730 to 2,200)
Tensile Strength, ISO 6922:
Steel (grit blasted) N/mm² 12 to 25
(psi) (1,700 to 3,600)
Buna-N N/mm² 5 to 15
(psi) (730 to 2,200)
Cured for 24 hours @ 22 °C, followed by 48 hours @ 120 °C, tested
@ 22 °C
Lap Shear Strength, ISO 4587:
Steel (grit blasted) N/mm² ≥18.0
LMS
(psi) (≥2,610)
TYPICAL ENVIRONMENTAL RESISTANCE
Cured for 1 week @ 22 °C
Lap Shear Strength, ISO 4587:
Steel (grit blasted)
Hot Strength
Tested at temperature
% Strength @ 22 °C
Temperature, °C
100
75
50
25
0
0 50 100 150
Heat Aging
Aged at temperature indicated and tested @ 22 °C
% Initial Strength @ 22 °C
Exposure Time, hours
125
100
75
50
25
0
0 1000 2000 3000 4000 5000
80 °C
100 °C
120 °C
Chemical/Solvent Resistance
Aged under conditions indicated and tested @ 22 °C.
% of initial strength
Environment °C 100 h 500 h 1000 h
Motor oil 40 85 85 85
Gasoline 22 90 70 70
Ethanol 22 95 95 80
Isopropanol 22 75 75 75
Freon TA 22 90 90 85
Heat/humidity 95% RH 40 80 80 65
Lap Shear Strength, ISO 4587:
Polycarbonate
% of initial strength
Environment °C 100 h 500 h 1000 h
Heat/humidity 95% RH 40 100 100 100
GENERAL INFORMATION
This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidizing materials.
For safe handling information on this product, consult the
Safety Data Sheet (SDS).
Directions for use:
1. For best performance bond surfaces should be clean and
free from grease.
2. This product performs best in thin bond gaps (0.05 mm).
3. Excess adhesive can be dissolved with Loctite cleanup
solvents, nitromethane or acetone.
Loctite Material Specification
LMS
LMS dated December-5, 2003. Test reports for each batch
are available for the indicated properties. LMS test reports
include selected QC test parameters considered appropriate to
specifications for customer use. Additionally, comprehensive
controls are in place to assure product quality and
consistency. Special customer specification requirements may
be coordinated through Henkel Quality.
Henkel Americas
+860.571.5100
Henkel Europe
+49.89.320800.1800
Henkel Asia Pacific
+86.21.2891.8859
For the most direct access to local sales and technical support visit: www.henkel.com/industrial