Datasheet
TDS LOCTITE
®
454™, February-2012
TYPICAL PERFORMANCE OF CURED MATERIAL
Adhesive Properties
Cured for 30 seconds @ 22 °C
Tensile Strength, ISO 6922:
Buna-N N/mm² ≥6.0
LMS
(psi) (≥870)
Cured for 72 hours @ 22 °C
Tensile Strength, ISO 6922:
Buna-N N/mm² 15.1
(psi) (2,190)
Lap Shear Strength, ISO 4587:
Steel (grit blasted) N/mm² 20.9
(psi) (3,030)
Aluminum (etched) N/mm² 17.1
(psi) (2,480)
Zinc dichromate N/mm² 11.5
(psi) (1,670)
ABS * N/mm² 8.3
* (psi) (1,200)
PVC * N/mm² 7.1
* (psi) (1,030)
Phenolic * N/mm² 12.3
* (psi) (1,780)
Polycarbonate N/mm² 7.7
(psi) (1,120)
Nitrile * N/mm² 1.3
* (psi) (190)
Neoprene * N/mm² 1.1
* (psi) (160)
Block Shear Strength, ISO 13445:
Polycarbonate N/mm² 9.6
(psi) (1,390)
ABS N/mm² 23.3
(psi) (3,380)
PVC N/mm² 3.3
(psi) (480)
Phenolic * N/mm² 6.7
* (psi) (970)
* substrate failure
TYPICAL ENVIRONMENTAL RESISTANCE
Cured for 1 week @ 22 °C
Lap Shear Strength, ISO 4587:
Steel (grit blasted)
Hot Strength
Tested at temperature
% Strength @ 22 °C
Temperature, °C
140
120
100
80
60
40
20
0
-40 -20 0 20 40 60 80 100 120 140
Heat Aging
Aged at temperature indicated and tested @ 22 °C
% Initial Strength @ 22 °C
Exposure Time, hours
125
100
75
50
25
0
0 250 500 1000
60 °C
80 °C
100 °C
120 °C
Chemical/Solvent Resistance
Aged under conditions indicated and tested @ 22 °C.
% of initial strength
Environment °C 100 h 500 h 1000 h
Motor oil 40 105 85 80
Unleaded gasoline 22 95 120 125
Water 22 75 70 75
Water/glycol 22 90 85 85
Ethanol 22 120 125 120
Isopropanol 22 100 130 135
98% RH 40 70 55 55
Chemical/Solvent Resistance
Aged under conditions indicated and tested @ 22°C.
Lap Shear Strength, ISO 4587, Polycarbonate
% of initial strength
Environment °C 100 h 500 h 1000 h
Air 22 105 105 105
98% RH 40 105 105 105
GENERAL INFORMATION
This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidizing materials.
For safe handling information on this product, consult the
Safety Data Sheet (SDS).
Directions for use:
1.
Bond areas should be clean and free from grease. Clean
all surfaces with a Loctite
®
cleaning solvent and allow to
dry.
2.
To improve bonding on low energy plastic surfaces,
Loctite
®
Primer may be applied to the bond area. Avoid
applying excess Primer. Allow the Primer to dry.
3.
LOCTITE
®
Activator may be used if necessary. Apply it to
one bond surface (do not apply activator to the primed
surface where Primer is also used). Allow the Activator to
dry.