Datasheet
TDS LOCTITE
®
222, January-2009
% of Full Strength on Steel
Cure Time
100
75
50
25
0
1min 5min10min 30min 1h 3h 6h 24h 72h
Activator 7471™
Activator 7649™
No activator
TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties:
Coefficient of Thermal Expansion,
ISO 11359-2, K
-1
80×10
-6
Coefficient of Thermal Conductivity, ISO 8302,
W/(m·K)
0.1
Specific Heat, kJ/(kg·K) 0.3
TYPICAL PERFORMANCE OF CURED MATERIAL
Adhesive Properties
After 24 hours @ 22 °C
Breakaway Torque, ISO 10964:
M10 steel nuts and bolts N·m 6
(lb.in.) (50)
Prevail Torque, ISO 10964:
M10 steel nuts and bolts N·m 4
(lb.in.) (35)
Breakloose Torque, ISO 10964, Pre-torqued to 5 N·m:
M10 steel nuts and bolts N·m 14
(lb.in.) (120)
Max. Prevail Torque, ISO 10964, Pre-torqued to 5 N·m:
M10 steel nuts and bolts N·m 14
(lb.in.) (120)
Compressive Shear Strength, ISO 10123:
Steel pins and collars N/mm² ≥2.5
LMS
(psi) (≥360)
TYPICAL ENVIRONMENTAL RESISTANCE
Cured for 1 week @ 22 °C
Breakloose Torque, ISO 10964, Pre-torqued to 5 N·m:
M10 zinc phosphate steel nuts and bolts
Hot Strength
Tested at temperature
% Strength @ 22 °C
Temperature, °C
100
75
50
25
0
0 50 100 150
Heat Aging
Aged at temperature indicated and tested @ 22 °C
% Initial Strength @ 22 °C
Exposure Time, hours
125
100
75
50
25
0
0 1000 2000 3000 4000 5000
120 °C
150 °C
Chemical/Solvent Resistance
Aged under conditions indicated and tested @ 22 °C.
% of initial strength
Environment °C 100 h 500 h 1000 h 5000 h
Motor oil (MIL-L-46152) 125 100 95 90 85
Leaded Petrol 22 95 95 95 95
Brake fluid 22 95 95 95 90
Water/glycol 50/50 87 80 80 80 80
Acetone 22 100 90 90 90
Ethanol 22 95 95 90 90
GENERAL INFORMATION
This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidizing materials
For safe handling information on this product, consult the
Material Safety Data Sheet (MSDS).
Where aqueous washing systems are used to clean the
surfaces before bonding, it is important to check for
compatibility of the washing solution with the adhesive. In
some cases these aqueous washes can affect the cure and
performance of the adhesive.
This product is not normally recommended for use on plastics
(particularly thermoplastic materials where stress cracking of
the plastic could result). Users are recommended to confirm
compatibility of the product with such substrates.
Directions for use: