Instruction Manual
HK-D
HK-D-BA-e-1311 3
Table 2
No.
Material
HLD
Strength σ
b
(MPa)
1 Mild steel
350～522 374～780
2
High-carbon steel
500～710 737～1670
3
Cr steel
500～730 707～1829
4
Cr-V steel
500～750 704～1980
5
Cr-Ni steel
500～750 763～2007
6
Cr-Mo steel
500～738 721～1875
7
Cr-Ni-Mo steel
540～738 844～1933
8
Cr-Mn-Si steel
500～750 755～1993
9
Super strength steel
630～800 1180～2652
10
Stainless steel
500～710 703～1676
1.3 Types and specification
No.
Remarks
Standard Delivery
1
Main unit
1
2 D type impact device 1
3
Small supporting ring
1
Additional
Optional Delivery
1
Communication cable
with
DataView Software ATC 01
2 Printer
3+4 Nylon brush1 and 2
2. in case of choosing G type
impact device
5
Various non-conventional types of impact
devices
See table 3
6
Various non-conventional types of impact
supporting rings
See table 4
Table 3
Non conventional
impact devices
DC(D)/DL D+15 C G
Impacting energy
Mass of impact
body
11Mj
5.5g/7.2g
11mJ
7.8g
2.7mJ
3.0g
90mJ
20.0g
Test tip Hardness
Diameter of test tip
Material of test tip
1600HV
3mm
Tungsten
carbide
1600HV
3mm
Tungsten
carbide
1600HV
3mm
Tungsten
carbide
1600HV
5mm
Tungsten
carbide
I
mpact device
Diameter
Impact device
Length
Impact device
Weight
20mm
86(147)/
75mm
50g
20mm
162mm
80g
20mm
141mm
75g
30mm
254mm
250g
Max. hardness of
workpiece
940HV 940HV 1000HV 650HB
Mean roughness of
workpiece surface of
the Ra
1.6μm 1.6μm 0.4μm 6.3μm