Manual

TDS LOCTITE
®
410™, March-2008
Cured for 24 hours @ 22 °C, followed by 24 hours @ 121 °C, tested
@ 22 °C
Lap Shear Strength, ISO 4587:
Steel (grit blasted) N/mm² ≥19.3
LMS
(psi) (≥2,800)
TYPICAL ENVIRONMENTAL RESISTANCE
After 1 week @ 22 °C
Lap Shear Strength, ISO 4587:
Mild steel (grit blasted)
Hot Strength
Tested at temperature
% Strength @ 22 °C
Temperature, °C
100
75
50
25
0
0 60 80 100 120
Heat Aging
Aged at temperature indicated and tested @ 22 °C
% Initial Strength @ 22 °C
Exposure Time, hours
150
125
100
75
50
25
0
24 100 500 1000 5000
80 °C
100 °C
Chemical/Solvent Resistance
Aged under conditions indicated and tested @ 22 °C.
% of initial strength
Environment °C 100 h 500 h 1000 h
Motor oil (MIL-L-46152) 40 85 85 85
Gasoline 22 90 70 70
Isopropanol 22 75 75 75
Industrial methylated
spirits
22 95 95 80
1,1,1 Trichloroethane 22 80 70 50
Freon TA 22 90 90 85
Heat/humidity 95% RH 40 100 100 100
GENERAL INFORMATION
This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidizing materials
For safe handling information on this product, consult the
Material Safety Data Sheet (MSDS).
Directions for use
1. For best performance bond surfaces should be clean and
free from grease.
2. This product performs best in thin bond gaps (0.05 mm).
3. Excess adhesive can be dissolved with Loctite cleanup
solvents, nitromethane or acetone.
Loctite Material Specification
LMS
LMS dated June-13, 2001. Test reports for each batch are
available for the indicated properties. LMS test reports include
selected QC test parameters considered appropriate to
specifications for customer use. Additionally, comprehensive
controls are in place to assure product quality and
consistency. Special customer specification requirements may
be coordinated through Henkel Quality.
Storage
Store product in the unopened container in a dry location.
Storage information may be indicated on the product container
labeling.
Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or
greater than 8 °C can adversely affect product properties.
Material removed from containers may be contaminated during
use. Do not return product to the original container. Henkel
Corporation cannot assume responsibility for product which
has been contaminated or stored under conditions other than
those previously indicated. If additional information is required,
please contact your local Technical Service Center or
Customer Service Representative.
Conversions
(°C x 1.8) + 32 = °F
kV/mm x 25.4 = V/mil
mm / 25.4 = inches
µm / 25.4 = mil
N x 0.225 = lb
N/mm x 5.71 = lb/in
N/mm² x 145 = psi
MPa x 145 = psi
N·m x 8.851 = lb·in
N·m x 0.738 = lb·ft
N·mm x 0.142 = oz·in
mPa·s = cP
Henkel Americas
+860.571.5100
Henkel Europe
+49.89.320800.1800
Henkel Asia Pacific
+86.21.2891.8863
For the most direct access to local sales and technical support visit: www.henkel.com/industrial
Documentation Provided By HMC Electronics
33 Springdale Ave. Canton, MA 02021
http://www.hmcelectronics.com
[phone]