SOCKET FUSION TIME CYCLES
American National Standard - ASTM F2620
Polyethylene (PE)
Temperature: 490 - 510 °F / 254 - 266 ℃
PIPE SIZE
PE80 MDPE
Medium Density Polyethylene -
PE 2406/PE 2708
PE100 HDPE
High Density Polyethylene - PE
3408/PE 3608/PE 4710
Pipe Size
Heating
Time
Fusion
Time
Cooling
Time
Heating
Time
Fusion
Time
Cooling
Time
Inches
mm
Sec.
Sec.
Sec.
Sec.
1/2"CTS
16
6-7
Immediate
30
6-10
Immediate
30
1/2"IPS
20
6-7
Immediate
30
6-10
Immediate
30
3/4"
25
6-7
Immediate
30
6-10
Immediate
30
1"
32
10-12
Immediate
30
15-17
Immediate
30
1 1/4"
40
12-14
Immediate
45
18-21
Immediate
60
1 1/2"
50
14-17
Immediate
45
20-23
Immediate
60
2"
63
16-19
Immediate
45
24-28
Immediate
60
2 1/2"
75
18-20
Immediate
45
24-28
Immediate
60
3"
90
20-24
Immediate
60
28-32
Immediate
75
4"
110
24-29
Immediate
60
32-37
Immediate
75
* Allow the joint to cool an additional five (5) minutes before exposing the joint to any type of
stresses.
NOTE: Some recommend using a 50-60 grit emery or garnet cloth to roughen the outside of
the pipe and inside of the fitting as a means of minimizing any possible skin interface when
making the fusion. Sandpaper is not recommended for this purpose, as it might disintegrate
and contaminate the joint interface.
Pipe chamfer(c) and Insert depth (d)
Pipe Size (s)
Pipe Chamfer
Insert depth
Inches
mm
(c)
(d)
1/2"CTS
16
2 mm
13 mm
1/2"IPS
20
14 mm
3/4"
25
15 mm
1"
32
17 mm
1 1/4"
40
18 mm
1 1/2"
50
20 mm
2"
63
3 mm
26 mm
2 1/2"
75
29 mm
3"
90
32 mm
4"
110
35 mm