User Manual

10
Tetric EvoCeram
G-ænial Universal Flo
Filtek Supreme XTE
EsthetX HD
Venus
G-ænial Flo
Filtek Supreme XT Flow
Tetric EvoFlow
01020304
05
0
0
10
20
30
40
50
60
70
80
90
100
0 2000 4000 6000 8000 10000 12000
Gloss value (%)
Tooth brush cycle (times)
Polished surface Un-polished (finished) surface
G-ænial Universal Flo Technical Manual
Figure 8: Three-body wear test of various
composite materials.
Source:GCCorporation,R&Ddepartment,Japan,
2010
Within the limitations of this test, it can
be concluded that the wear resistance
of G-ænial Universal Flo is superior
to all tested flowable and putty-like
composites with the exception of
Filtek Supreme XTE which
demonstrated similar results.
G-ænial Universal Flo exhibits an exceptional ability to resist wear, superior to most putty-like
composites on the market.
6.4 Polishability
Tooth brush abrasion test set up:
The toothbrush abrasion test was performed on polished and unpolished surfaces of G-ænial
Universal Flo using a GC Prospec hard toothbrush and White & White dentifrice, under a load of
200 g for 12,000 cycles (equivalent to 1 year, assuming 15 laps twice daily).
6.4.1 G-ænial Universal Flo
gloss rate over time
Figure 9: Gloss rate after Toothbrush Abrasion
test of polished and unpolished surfaces of
G-ænial Universal Flo.
Source: GC Corporation, R&D department,
Japan,2010
The toothbrush abrasion test shows
that the gloss rate that can be
achieved with G-ænial Universal Flo
after toothbrushing cycles is the
same regardless of whether or not
the samples were originally polished.
G-ænial Universal Flo offers a unique self-polishing property, such that even unpolished
surfaces will gain and maintain gloss over time.
Three-body wear (µm)
Gloss rate after toothbrush abrasion test