SDS

湖南炬神電子有限公司
HU NAN GIANTSUN POWER ELECTRONICS CO., LTD
14
4.3.2 reliability
可靠性
表五
1
Vibration Test
振動測試
After standard charging, fixed the cell to
vibration table and subjected to vibration
cycling that the frequency is to be varied at
the rate of 1Hz per minute between 10Hz an 55Hz,
the excursion of the vibration is 1.6mm. The
cell shall be vibrated for 30 minutes per axis
of XYZ axes.
將標準充電後的電芯固定在振動臺上，沿 X、Y、Z
三個方向各振動 30 分鐘，振幅 1.6mm，振動頻率為
10Hz～55Hz，每分鐘變化 1Hz。
No leakage、，No fire
無洩漏、不起火
2
Drop Test
跌落測試
The cell is to be dropped from a height of 1.0
meter twice onto wooden concrete ground.
將標準充電後的電芯從 1.0 米高度跌落至木板地面
2 次
No explosion， no
fire， no leakage.
無爆炸、起火 、洩漏
3
pressure test
挤压测试
When the battery is fully charged, the battery
will be placed in the two plane perpendicular
to the direction of plate extrusion, extrusion
pressure between two plates applied 13.O kN +
078kN. Once the pressure reaches the maximum
value to stop the extrusion experiment,
external short-circuit the battery can not be
in the process of the experiment.
电池充满电后,将电池置于两个平面内,垂直于极
板方向进行挤压,两平板间施加 13.O kN± 078kN
的挤压力。一旦压力达到最大值即可停止挤压试
验,试验过程中电池不能发生外部短路。
The battery should be
no fire, no
explosion.
电池应不起火、不爆
炸。
4
External Short
外部短路
When the battery is fully charged, the battery
negative pole terminal short circuit, external
short circuit for total resistance (80 + 20)
m, the battery short circuit 24h.
电池充满电后,短路电池组的正负极端子,外部短
路总电阻为(80± 20)mΩ ，对电池组短路 24h。
The battery should be
no fire, no
explosion, no
leakage.
电池组应不起火、不爆
炸、不漏液。
5
重物冲击
将电池组按照 4.3.1 规定的试验方法充满电后,将
电池置于平台表面,将直径为 158mm± 02mm 的金属
棒横置在电池几何中心上表面,采用质量为 91kg±
01kg 的重物从 610mm± 25mm 的高处自由落体状态
撞击放有金属棒的电池表面,并观察 6h。要求电池
冲击试验时使其纵轴向与重物表面平行,金属棒与
电池纵轴向垂直。1 个样品只做一次冲击试验。
电池应不起火、不爆
炸。
6
温度循环
将电池组按照 4.3.1 规定的试验方法充满电后,将
电池放置在温度为 20℃ ±5℃ 的可控温的箱体中
进行如下步骤：
a)将样品放人温度为 75℃ ±2℃ 的实验箱中保持
6h;
b) 后将实验箱温度降为-40℃ ±2℃ ,并保持 6h;
电池应不起火、不爆
炸、不漏液.