TECHNICAL DATA SHEET ergo 5923
LOW ODOUR
Description
Medium to high viscous and nearly odourless glue, which shows less blooming or whitening
than normal grades. Suitable for bonding of jewellery or crystal into carrier and
r ecommended, wherever visible traces of glue must be avoided.
Physical Properties (liquid product)
Chemical Base: Cyanoacrylicacid-alkoxyethylester
Colour: clear/ colourless to pale yellow
Viscosity: 850 - 1200 mPas at 25°C
Density: 1.05 – 1,08 g/cm³ DIN 51757
Flashpoint: 87°C DIN 55213
Shelf Life: 12 month at room temperature
Fixture Time on :
Aluminium / Aluminium: 90 -110 seconds
SBR / SBR - rubber: 25 - 40 seconds
Polycarbonate / Polycarbonate: 25 - 35 seconds
EPDM / EPDM - rubber: 20 - 35 seconds
Final strength: 24 hours
Physical Properties (cured film)
Tensile Shear Strength on:
Aluminium / Aluminium: > 12 N/mm² DIN EN 1465
Tensile Force on round rubber profiles:
SBR /SBR - rubber ø18mm: > 1400 N
SBR / SBR 10 Tage/70°C: > 850 N
EPDM / EPDM - rubber ø16mm: > 200 N
EPDM / EPDM 10 Tage/70°C: > 150 N
Thermal Range: - 30°C up to +100°C
Melting point: + 165°C
WARRANTY INFORMATION - PLEASE READ CAREFULLY
The information contained herein is offered in good faith and is believed to be accurate. However, because conditions and methods of use of our
products are beyond our control, this information should not be used in substitution for customer's tests to ensure that KISLING products are safe,
effective, and fully satisfactory for the intended end use. KISLING sole warranty is that the product will meet the KISLING sales specifications in
effect at the time of shipment. Your exclusive remedy for breach of such warranty is limited to refund of purchase price or replacement of any
product shown to be other than as warranted. KISLING specifically disclaims any other express or implied warranty of fitness for a particular purpose
or merchantability. Unless KISLING provides you with a specific, duly signed endorsement of fitness for use, KISLING disclaims liability for any
incidental or consequential damages. Suggestions of uses should not be taken as inducements to infringe any particular patent.