Datasheet

Page 2

Cured Properties:

Colour (Mixed System)

Water White

Cured Density (g/ml)

1.04

Temperature Range (°C)

-60 to +200

Max Temperature Range

(Short Term (°C)/30

Mins) (Application and Geometry Dependent)

+250

Shore Hardness

A20

Flame Retardancy

Yes, meets UL94 HB

Tensile Strength (MPa)

1.27

Volume resistivity (ohm-cm)

Dielectric constant @ 50Hz

3.0

Dielectric dissipation factor @ 50 Hz

0.0026

Water absorption

(9.7mm thick disk, 51mm diameter)

10 days @ 20°C / 1 hour @ 100°C

<0.1% / <0.1%

Elongation At Break

100%

Mixing Procedures

All surfaces must be clean before resin is applied. Due to its moisture cure nature, the speed of the cure is

dependent on humidity and the thickness of the layer applied, hence thinner films will cure relatively quickly. At

a depth of greater than 3cm, SC3001 may take up to 7 days to achieve full cure properties.

Resin Packs

When in Resin pack form, the resin and hardener are mixed by removing the clip and moving the contents

around inside the pack until thoroughly mixed. To remove the clip, remove both end caps, grip each end of the

pack and pull apart gently. By using the removed clip, take special care to push unmixed material from the

corners of the pack. Mixing normally takes from two to four minutes depending on the skill of the operator and

the size of the pack. Both the resin and hardener are evacuated prior to packing so the system is ready for use

immediately after mixing. The corner may be cut from the pack so that it may be used as a simple dispenser.