Datasheet

Page 2
Cured System:
Thermal Conductivity (W/m.K)
1.26
Cured Density (g/ml)
2.09
Temperature Range (°C)
-40 to +130
Max Temperature Range
(Short Term (°C)/30 Mins)
(Application and Geometry Dependent)
+150
Dielectric Strength (kV/mm)
10
Volume Resistivity (ohm-cm) 10
15
Shore Hardness
D80
Colour (Mixed System)
White
Flame Retardancy
Meets UL94 V-0
Tensile Strength (MPa)
82
Compressive Strength (MPa)
120
Deflection Temperature (°C)
60
Coefficient of Expansion (ppm/°C)
30
Loss Tangent @ 50 Hz
0.05
Permittivity @ 50 Hz
6.00
Comparative Tracking Index
>850 Volts
Water Absorption
(9.7mm thick disk, 51mm diameter)
10 days @ 20ºC / 1 hour @ 100ºC
< 0.5% / < 1%
Elongation At Break
0.3%
Mixing Procedures
Resin Packs
When in Resin pack form, the resin and hardener are mixed by removing the clip and moving the contents
around inside the pack until thoroughly mixed. To remove the clip, remove both end caps, grip each end of the
pack and pull apart gently. By using the removed clip, take special care to push unmixed material from the
corners of the pack. Mixing normally takes from two to four minutes depending on the skill of the operator and
the size of the pack. Both the resin and hardener are evacuated prior to packing so the system is ready for use
immediately after mixing. The corner may be cut from the pack so that it may be used as a simple dispenser.