Flexinol® Technical Data
Diameter Size (Inches)
Resistance (Ohms/
Inch)
Maximum Pull Force
(grams)
Approximate* Current
at Room Temperature
(mA)
Contraction* Time
(seconds)
Off Time LT=70° C
Wire** (seconds)
Off Time HT=90° C
Wire** (seconds)
0.0010 45.0 7 20 1 0.10 0.06
0.0015 21.0 17 30 1 0.25 0.09
0.002 12.0 35 50 1 0.3 0.1
0.003 5.0 80 100 1 0.5 0.2
0.004 3.0 150 180 1 0.8 0.4
0.005 1.8 230 250 1 1.6 0.9
0.006 1.3 330 400 1 2.0 1.2
0.008 0.8 590 610 1 3.5 2.2
0.010 0.5 930 1000 1 5.5 3.5
0.012 0.33 1250 1750 1 8.0 6.0
0.015 0.2 2000 2750 1 13.0 10.0
0.020 0.16 3562 4000 1 17.0 14.0
Flexinol® Technical Data
If Flexinol® actuator wire is used within the guidelines then obtaining repeatable motion from the wire for tens of mil-
lions of cycles is reasonable. If higher stresses or strains are imposed, then the memory strain is likely to slowly decrease
and good motion may be obtained for only hundreds or a few thousand of cycles. The permanent deformation, which
occurs in the wire during cycling, is heavily a function of the stress imposed and the temperature under which the actua-
tor wire is operating. Flexinol® wire has been specially processed to minimize this straining, but if the stress is too great
or the temperature too high some permanent strain will occur. Since temperature is directly related to current density
passing through the wire, care should be taken to heat, but not overheat, the actuator wire. The following chart gives
rough guidelines as to how much current and force to expect with various wire sizes.
* The contraction time is directly related to current input. The figures used here are only approximate since room temperatures, air
currents, and heat sinking of specific devices vary. On small diameter wires (</= 0.006" diameter) currents which heat the wire in 1
second can typically be left on without over-heating it. Both heating and cooling can be dramatically changed (see section 3 of the
technical characteristics in the standard literature for more information.)
** Approximate cooling time.