Datasheet

CECMarket Specific Products
Non Flame
retardant
>2:1
Shrink Ratio
77
www.dsg-canusa.de
Ordering: Specify the product name plus each of the following options: 1) Size 2) Colour 3) Total Quantity 4) Printing Options
For example: CEC 36/55 black, 1.075 pcs., unprinted
76
Adhesive-lined heat shrinkable
end cap which enables easy pro-
tection and sealing of unused
cables from environmental effects
Unaffected by ultraviolet light
Good chemical and solvent
resistance
Thermoplastic liner provides
complete environmental seal
Continuous Operating
Temperature: -55°C to 100°C
Shrink Temperature: 120°C
Features
CEC
CEC
Crosslinked Polyolefin End Cap
mm mm mm mm mm
CEC 15/4,5 15,0 4,5 45,0 1,0 5,0 - 12,0
CEC 25/9 25,0 9,0 70,0 2,7 10,0 - 22,0
CEC 36/15 36,0 15,0 95,0 2,8 17,0 - 30,0
CEC 63/24 63,0 24,0 110,0 3,6 28,0 - 55,0
CEC 80/40 80,0 40,0 130,0 3,6 45,0 - 70,0
CEC 102/60 102,0 60,0 152,0 3,6 68,0 - 90,0
CEC 124/60 124,0 60,0 152,0 3,6 75,0 - 110,0
CEC 148/57 148,0 57,0 152,0 4,5 80,0 - 135,0
* Internal diameter without adhesive coating
INTERNAL DIAMETER* (MAX)
A
LENGTH (MIN)
B
ORDER REF. NO. EXPANDED RECOVERED
WALL THICKNESS (MIN)
T
GENERAL USE DIAMETER
Dimensions
Physical
Property
Test Method Typical Performance
Technical Data
Electrical
Property Test Method Typical Performance
Dielectric Strength IEC - 243 12 kV/mm min.
Volume Resistivity IEC - 93 10
11
Ω x cm
Standard Colours Special Colours
black On request
good good good
Printability Hot stamp Ink jet Offset
INTERNAL DIAMETER* (MIN)
A
Tensile Strength ASTM-D 638 M 12,0 MPa min.
Elongation ASTM-D 638 M 300% min.
Water Absorption ISO - 62 1,0% max.
Shore Hardness ASTM-D 2240 45 Shore D min.
Tensile Strength after Heat
Aging (168 hrs at 120°C) ISO - 188 10,0 MPa min.
Elongation after Heat Aging
(168 hrs at 120°C) ISO - 188 250% min.
08/2007