Item Brochure

121 Kelsey Lane | Suite G | Tampa, Florida 33619
Customer Service: 800-473-1200 | [e-mail]
The Dietzgen Corporation ©
733
20LB BOND PAPER
(RECYCLED)
DESCRIPTION
733 is 20LB everyday production bond paper featuring
a smooth bright white surface and made from 30% re-
cycled content. 733 provides good ink adhesion, print
quality, line acuity and image clarity across multiple print
technologies.
Recycled paper helps conserve energy, reduce solid
waste, decrease pollution, improve the quality of waste
water thereby reducing pressure on the forests and the
environment and improving health standards.
PHYSICAL CHARACTERISTICS
Caliper 4 mil
Basis Weight 75 g/m2
Bond Weight 20LB
Brightness 92
Finish Matte
Opacity 88%
Whiteness 145 (CIE)
Smoothness 170
Lab Values NA
Base material Paper
Structure Uncoated
PH Acid Free / ECF
*All values are for reference only
FEATURES AND BENEFITS
- Good print performance
- Good ink adhesion
- Good line acuity
- Good Image sharpness
- Good black density
- Smooth matte fi nish
- Acid free
- Elemental chlorine free (ECF)
- Meets ANSI Type I OCR dirt guidelines
- Meets ANSI Type III fl uorescence guidelines
- 30% post-consumer waste content
PROCESSING TIPS
- Preferred side out
FINISHING & PRINTING
- Compatible with pressure sensitive, heat assist and
thermal overlaminates.
- Allow su cient time for inkjet prints to completely dry
before rolling, laminating or cutting.
- Use a sharp blade to prevent ink and toner fl aking on
the edges
- Overlamination is not required. However, it can
provide additional surface protection from dirt,
abrasion and moisture.
- Can use pen / pencil to write on surface
- Compatible with common stapling and binding
equipment
SHELF LIFE
2 years from ship date
STORAGE CONDITIONS
Temperature 50-85° F (10-30° C)
Relative Humidity 30-65%
OPTIMAL SERVICE ENVIRONMENT
Temperature 50-85° F (10-30° C)
Relative Humidity 30-65%
BOND PAPER
PRINTER COMPATIBILITY
*For additional information visit www.dietzgen.com
*Does not guarantee optimal performance
PRODUCT DATA SHEET
Rev 2 - Updated 8/17