Data Sheet

Flat On its edge Upright
Tensile strength ISO 527 62.9 MPa / 9.1 ksi - 19.1 MPa / 2.8 ksi
Elongation at Break ISO 527 2.9 % - 0.8 %
Young’s Modulus ISO 527 5052 MPa / 733 ksi - 2455 MPa / 356 ksi
Flexural Strength ISO 178 125.1 MPa / 18.1 ksi 121.9 MPa / 17.7 ksi 56.0 MPa / 8.1 ksi
Flexural Modulus ISO 178 6063 MPa / 879 ksi 6260 MPa / 908 ksi 2190 MPa / 318 ksi
Flexural Strain at Break ISO 178 No break 3.6 % 4.0 %
Impact Strength Charpy (notched) ISO 179-2 5.1 kJ/m2 5.3 kJ/m2 1.6 kJ/m2
Impact Strength Charpy (unnotched) ISO 179-2 21.9 kJ/m2 20.4 kJ/m2 2.8 kJ/m2
Impact Strength Izod (notched) ISO 180 6.5 kJ/m2 5.8 kJ/m2 -
Impact Strength Izod (unnotched) ISO 180 16.3 kJ/m2 15.1 kJ/m2 4.1 kJ/m2
PAHTCF - Technical information including:
HDT at 1.8 MPa (dry) 92 °C / 198 °F ISO 75-2
HDT at 0.45 MPa (dry) 145 °C / 293 °F ISO 75-2
HDT at 1.8 MPa (conditioned) 91 °C / 196 °F ISO 75-2
HDT at 0.45 MPa (conditioned) 128 °C / 262 °F ISO 75-2
Glass Transition Temperature 70 °C / 158 °F ISO 11357-2
Crystallization Temperature 180 °C / 356 °F ISO 11357-3
Melting Temperature 234 °C / 453 °F ISO 11357-3
Melt Volume Flow Rate 42.2 cm3/10min / 2.6 in3/10min (275°C/5kg) ISO 1133
General Properties
Thermal Properties
Mechanical Properties | Conditioned specimens
Standard
Standard
Printed Part Density (dry) 1232 kg/m3 / 76.9 lb/ft3 ISO 1183-1
Printed Part Density (conditioned) 1234 kg/m3 / 77.0 lb/ft3 ISO 1183-1
Print direction Standard XY XZ ZX