Data Sheet

HDT at 1.8 MPa (dry) 6v5 °C / 149 °F ISO 75-2
HDT at 0.45 MPa (dry) 135 °C / 275 °F ISO 75-2
Vicat softening point at 50 N 172 °C / 342 °F ISO 306
Glass Transition Temperature 49 °C / 120 °F ISO 11357-2
Crystallization Temperature 147 °C / 297 °F ISO 11357-3
Melting Temperature 195 – 197 °C / 383 – 386 °F ISO 11357-3
Melt Volume Rate 49.5 cm3 /10 min / 3.02 in3 /10 min (275 °C, 5 kg) ISO 1133
PA - Technical information including:
General Properties
Thermal Properties
Mechanical Properties | Conditioned specimens
Standard
Standard
Printed Part Density (dry)
Print direction Standard XY XZ ZX
1115 kg/m3 / 69.6 lb/ft3 ISO 1183-1
Printed Part Density (conditioned) 1050 kg/m3 / 65.5 lb/ft3 ISO 1183-1
Tensile strength ISO 527 33.2 MPa / 4.8 ksi - 17.6 MPa / 2.6 ksi
Elongation at Break ISO 527 143.3% - 12.8%
Young’s Modulus ISO 527 395 MPa / 57 ksi - 334 MPa / 48 ksi
Flexural Strength ISO 178 17.7 MPa / 2.6 ksi# 18.1 MPa / 2.6 ksi # 17.3 MPa / 2.5 ksi #
Flexural Modulus ISO 178 445 MPa / 64.5 ksi 468 MPa / 67.9 ksi 428 MPa / 62.1 ksi
Flexural Strain at Break ISO 178 No break No break No break
Impact Strength Charpy (notched) ISO 179-2 - 136 kJ/m2 ## 9.4 kJ/m2
Impact Strength Charpy (unnotched) ISO 179-2 No break No break 13.4 kJ/m2
Impact Strength Izod (notched) ISO 180 85.4 kJ/m2 106.0 kJ/m2 10.1 kJ/m2
Impact Strength Izod (unnotched) ISO 180 No break No break 17.4 kJ/m2
# No break, strength at 5% bending strain
## Partial rupture