Data Sheet

Flat On its edge Upright
Tensile strength ISO 527 29.5 MPa / 4.3 ksi - 17.9 MPa / 2.6 ksi
Elongation at Break ISO 527 10.9 % - 2.1 %
Young’s Modulus ISO 527 1379 MPa / 200 ksi - 1106 MPa / 160 ksi
Flexural Strength ISO 178 48.3 MPa / 7.0 ksi 48.7 MPa / 7.1 ksi 23.1 MPa / 3.4 ksi
Flexural Modulus ISO 178 1406 MPa / 204 ksi 1133 MPa / 164 ksi 878 MPa / 127 ksi
Flexural Strain at Break ISO 178 5.6 % 5.9 % 2.7 %
Impact Strength Charpy (notched) ISO 179-2 32.0 kJ/m2 41.9 kJ/m2 2.5 kJ/m2
Impact Strength Charpy (unnotched) ISO 179-2 71.9 kJ/m2 118.7 kJ/m2 6.9 kJ/m2
Impact Strength Izod (notched) ISO 180 26.4 kJ/m2 38.4 kJ/m2 2.2 kJ/m2
Impact Strength Izod (unnotched) ISO 180 73.1 kJ/m2 131.1 kJ/m2 6.6 kJ/m2
ABS - Technical information including:
HDT at 1.8 MPa 71 °C / 160 °F ISO 75-2
HDT at 0.45 MPa 91 °C / 196 °F ISO 75-2
Glass Transition Temperature 80 and 114 °C / 176 and 237 °F ISO 11357-2
Melt Volume Rate 10.0 cm3 /10 min / 0.61 in3 /10 min (250 °C, 5 kg) ISO 1133
General Properties
Thermal Properties
Mechanical Properties | Conditioned specimens
Standard
Standard
Printed Part Density 1075 kg/m3 / 67.1 lb/ft3 ISO 1183-1
Print direction Standard XY XZ ZX