Property Profile
Table 4: Typical properties for Lexan Polycarbonate Sheet
Property Physical Test method Unit Value
Density ISO 1183 lbs/in
3
0,043
Water absorption, 50% RH / 23°C ISO62 % 0,15
Water absorption, saturation / 23°C ISO 62 % 0,35
Mechanical
Tensile stress at yield 1,97"/min ISO 527 MPa 60
Tensile stress at break 1,97"/min ISO 527 MPa 70
Tensile strain at yield 1,97"/min ISO 527 % 6
Tensile strain at break 1,97"/min ISO 527 % 120
Tensile modulus 0,079"/min ISO 527 MPa 2300
Flexural stress at yield 0,079"/min ISO 178 MPa 90
Flexural stress at break 0,079/min ISO 178 MPa 2300
Hardness H358/30 95 ISO 2039/1 MPa 95
Thermal
Vicat Softening Temperature, rate B/120 ISO 306 °F 293
HTD/Ae, 1.8 MPa edgew. 120*1*04/sp=100 ISO 75 °F 260,6
Thermal conductivity ISO 8302 BTU/hr ft °F 0,116
Coeff. of lin. Therm. Exp.extr. 23-80°C ISO 11359-2 1/°F 4.00 E-05
Electrical
Volume resistivity IEC 60093 Ohm.in 5,9 E15
These property values have been derived from Lexan resin data for the material used to produce this sheet product.
Variation within normal tolerances are possible for various colors. These typical values are not intended for specication purposes.
If minimum certiable properties are required please contact your local SABIC Innovative Plastics, Specialty Film & sheet
representative. All values are measured at least after 48 hours storage at 23°C/50% relative humidity. All properties are measured on injection
molded samples. All samples are prepared according ISO 294.