Product Manual

No. 1188 - 02/17
MRO BRITE GALVANIZE COATING
PRODUCT NUMBERS: 188 - 12 OZ. NET WT. AEROSOL
I. GENERAL DESCRIPTION
Description: Aervoe's MRO Brite Galvanize Coating is
a cost effective way to repair hot-dip galvanizing that has
been damaged by abrasion, scratching, cutting or welding.
Cosmetically repairs both ferrous and nonferrous surfaces.
Uses zinc metallic ake that is 97% pure. An exceptionally
smooth-owing product that leaves a bright metal coating
with a reective metallic sheen containing 65% zinc in the
dry lm. The Zinc fuses to metal substrates to provide
protection similar to hot-dip galvanizing.
Benets: Restores galvanized surfaces to the bright look
of hot-dip. Stops rust and corrosion on any iron or steel
surface. Even if the surface is scratched, the zinc surface
will continue to protect against corrosion. Brite Galvanize
offers the convenience of on-the-job application when
hot-dip repair is necessary. Acceptable as a coating in
federally inspected meat and poultry plants for application to
structural surfaces where there is a possibility of incidental
food contact. Does not contain lead, chromates, methylene
chloride or uorocarbons. Meets performance requirements
of ASTM A780.
Application: Use on pipes, heavy equipment, highway
guard rails, hand rails, welds, metal chain fences, bridges,
storage tanks, corrugated metal buildings, transformers,
television towers, signs and sign posts, railroad equipment,
construction equipment and anywhere the bright look of
hot-dipped surfaces is desired.
Directions: Whenever possible, repair should be applied
within two hours of the damage to the galvanized surface;
this prevents oxidation of the exposed areas. Surface
should be free of dirt, dust, oil, grease, old paint, heavy mill
scale, loose rust particles and any other contaminants that
could prevent proper adhesion. Severely rusted areas
should be cleaned with a wire brush to remove loose
scale prior to application of MRO Brite Galvanize. For
best results, repair material should extend at least three
inches beyond edges of the damaged area to ensure
continuity of galvanic action and used at temperatures
between 60° and 80°F (16° to 27°C). Drying may be
accelerated by applying heat. Align spray head with
black mark on valve rim to insure complete evacuation
of contents. Vigorously shake can for 2 minutes after
hearing rattle of agitator ball (ball should release in 10 to
30 seconds), and intermittently (1 to 2 seconds) during
use. Apply from a distance of 8 to 12 inches. Spray in
light, sweeping strokes to avoid run and sags. Two light
coats are better than one heavy coat. Whenever you must
set the aerosol can aside for more than 2 minutes or are
ready to store the can, then invert the can and spray for
two seconds to clear dip tube, valve and tip to prevent
zinc from drying in those areas.
Limitations: Please refer to the Safety Data Sheet for
specic information on material hazards, etc. Do not apply
at temperatures below 40°F (4°C), or if rain is imminent
within 6 hours of application. Galvanizing products have a
limited shelf life; use them within 12 months from the date
of manufacture (guarantee is for 6 months from date of
purchase and 12 months from date of manufacture).
Packaging:
Aerosol: Cans (211x604) 12 net wt. (340 g) 13.6 . oz. (402 ml)
Case (12/case): 13 lbs. (5.9 kg) 0.47 CF (0.013 CM)
Product Data Sheet
Aervoe Industries, Inc.
P.O. Box 485, Gardnerville, NV 89410
[phone] Phone • [phone] Fax • [phone] Customer Service
www.aervoe.com • [e-mail]
AEROSOL CARB VOC <80% / MIR < 1.25