Datasheet

Corrosion protection
on: pipes and
supports, welds on
bitumen protected
pipes, cable racks,
switch an control
cabinets, battery
containers.
Black
400 ml
Modified styrene-
butadiene rubber (SBR)
Aromatic hydrocarbons
Petroleum distillates
Propane butane
Excellent
None
N/A
1-2 hours
about 4 hours
80° C
Build up layer
thickness slowly and
evenly. No
deterioration of the
layer at thicknesses up
to about 3mm. When
sprayed at a distance
of 30 to 40 cm, an
application width of 5
to 8 cm is produced.
1600
Anti-Corrosion
Spray
1601 Sealer (clear) 1602 Sealer Red
1603 Sealer Black
1604 Sealer Grey
1605
Dehumidifier Spray
1609 Silicon
e
Lubricant
1617 Zinc Spray
As a protective coating
on electrical
connections, switches,
switchgear, terminal
boards, electronic
components, printed
circuits, coils,
windings and
laminated cores. In
addition, for use on
electrical equipment in
vehicules and for
repairing electric
motors. Also suitable
as a flexible covering
on construction
drawings and similar
items.
Clear
400 ml
Modified acrylic resin
Aliphatic and aromatic
hydrocarbons
Propane butane
Excellent
Slight
40kV/mm
15 minutes
120 minutes
After 700
hours/+120°C
1 x 10
12
cm
Surfaces to be coated
must be clean and
grease-free.
Application
Colour
Content
Base
Solvent
Propellant
Adhesion
Moisture absorption
Dielectric strength
Hardening at room
temperature:
dust dry
fully hardened
Temperature
stability
Surface resistance
Processing
Electrical and
electronic equipment,
switches, relays,
motors, batteries,
ignition systems,
tools, instruments,
threads, etc.
Beige
400 ml
Trated heavy napthenic
petroleum distillate
Aliphatic hydrocarbons
Petroleum distillates
Propane butane
Very good
Slight
N/A
N/A
-74°C to + 175°C
N/A
Dehumidification:
spray a thin film onto
the surface. After
about 30 seconds, the
moisture will dry out.
Where necessary,
repeat the process.
Corrosion protection:
apply a medium thick
film, where necessary,
repeat the process.
Defrosting: apply a
thick layer. After 15 to
30 seconds, repeat
where necessary.
The enclosed spray
pipe permits access to
difficult to reach areas.
Lubrication: el
equipment, lo
c
hinges, other
m
parts. Protecti
moisture and
corrosion end
a
plant and equi
polished surfa
shafts, plastic
,
leather, etc.
Clear
400 ml
Silicone oil
Petroleum dis
t
Propane buta
n
Very good
None
N/A
N/A
-32°C to + 17
7
N/A
The enclosed
s
pipe permits a
difficult to rea
c
Through
electrochemical
bonding with metal, it
provides lasting
protection against rust
and corrosion, even
on damaged surfaces.
Ideal as a protective
covering and as a
primer for exposed
metal construction.
Damaged zinc layers
can be repaired quite
easily.
Grey
400 ml
Zinc dust
Aliphatic and aromatic
hydrocarbons
Propane butane
Excellent
Slight
N/A
15 minutes
120 minutes
Up to 500°C
N/A
Surfaces to be coated
must be clean and
greas-free. Prior
cleaning is
recommended with
Scotch™ 1626 or
Scotch™ 1625.
As a protective coating
on electrical
connections, switches,
switchgear, terminal
boards, electronic
components, printed
circuits, coils, and
windings. In addition,
for use on electrical
equipment in vehicules
and for the repair of
electric motors.
Red
400 ml
Modified acrylic resin
Aliphatic and aromatic
hydrocarbons
Propane butane
Excellent
Slight
34kV/mm
15 minutes
60 minutes
After 700
hours/+120°C
N/A
Surfaces to be coated
must be clean and
grease-free.
Protective sprays : Insulating sprays : Preventative
maintenance spray
s